Product Details:
Thickness | 8-100mm |
Material | Steel |
Material Grade | A516 Gr.60, Gr.65, Gr.70,P235GH, P265GH, P295GH, P355NH,P275NH, P355NL1 |
Technique | Hot rolled |
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Others |
622B | 0.09/0.15 | 0.5 | 0.30/0.60 | 0.025 | 0.015 | 2.00/2.50 | 0.90/1.10 | 0.3 | 0.32 |
Grade | Thickness | Tensile Strength | Yield Strength | Elongation (A) |
622B | ≤100 | 515/690 | 310 | 16 |
>100 ≤150 | 500/670 | 285 | 16 |
Product Details:
Thickness | 10-100 mm |
Material | Steel |
Material Grade | A516 Gr.60, Gr.65, Gr.70,P235GH, P265GH, P295GH, P355NH,P275NH, P355NL1 |
Technique | Hot rolled, cold rolled |
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Nb | Ti | V | Al | N | Cu |
13CrMo45 | 0.08/0.18 | 0.35 | 0.40/1.00 | 0.025 | 0.01 | 0.70/1.15 | 0.40/0.60 | – | – | – | – | – | 0.012 | 0.3 |
Grade | Thickness | Yield Strength | Tensile Strength | Elongation (A) | Impact energy KV at test temperature | ||
-20°C | 0°C | +20°C | |||||
mm | MPa | MPa | % | J | J | J | |
13CrMo45 | ≤16 | 300 | 450/600 | 19 | – | – | 31 |
>16 ≤60 | 290 | 450/600 | 19 | - | - | 31 | |
>60 ≤100 | 270 | 440/590 | - | - | - | 27 | |
>100 ≤150 | 255 | 430/580 | - | - | - | 27 | |
>150 ≤250 | 245 | 420/570 | - | - | - | 27 |
Product Details:
Thickness | 5-100 mm |
Width | 1500-3500mm |
Length | 3000-18000mm |
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Others |
620B | 0.09/0.18 | 0.15/0.40 | 0.40/0.65 | 0.025 | 0.015 | 0.80/1.15 | 0.45/0.60 | 0.3 | 0.32 |
Grade | Thickness | Tensile Strength | Yield Strength | Elongation (A) |
620B | ≤75 | 480/600 | 340 | 18 |
>75 ≤100 | 450/570 | 280 | 16 | |
>100 ≤150 | 430/550 | 255 | 16 |
Product Details:
Thickness | 5-100 mm |
Material | Steel |
Standard | AISI, ASTM, BS, DIN, GB, JIS |
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Others |
621B | 0.09/0.17 | 0.50/0.80 | 0.40/0.65 | 0.025 | 0.015 | 1.00/1.50 | 0.45/0.60 | 0.3 | 0.32 |
Grade | Thickness | Tensile Strength | Yield Strength | Elongation (A) |
621B | ≤75 | 515/690 | 340 | 18 |
>75 ≤100 | 500/670 | 320 | 16 | |
>100 ≤150 | 490/650 | 310 | 16 |
Product Details:
Thickness | 2.3-100 mm |
Width | 1500-3500mm |
Length | 3000-18000mm |
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Nb | Ti | V | Al | N | Cu |
10CrMo910 | 0.08/0.14 | 0.5 | 0.40/0.80 | 0.02 | 0.01 | 2.00/2.50 | 0.90/1.10 | – | – | – | – | – | 0.012 | 0.3 |
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Thickness | 5-100mm |
Grade | SA 387 Gr.22 |
Surface | Plain Surface |
Finishing | Hot Rolled Finished |
Density | 8.00 |
Condition | Refurbished |
Weight | 8.00 |
Color | Red |
Material | Steel Plate |
Width | 1250-2500 mm |
BS | EN | ASTM/ASME | DIN |
622-515B | 10 CRMO910 | SA387-22-2 | 10 CRMO910 |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade 22 | 2.25% | 1.00% |
Element | - | Chemical Composition (%) |
- | SA387 Grade 22 | |
Carbon: | Heat Analysis: | 0.05 – 0.15 |
Product Analysis: | 0.04 – 0.15 | |
Manganese: | Heat Analysis: | 0.30 – 0.60 |
Product Analysis: | 0.25 – 0.66 | |
Phosphorus: | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Sulphur (max): | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Silicon: | Heat Analysis: | 0.50 max |
Product Analysis: | 0.50 max | |
Chromium: | Heat Analysis: | 2.00 – 2.50 |
Product Analysis: | 1.88 – 2.62 | |
Molybdenum: | Heat Analysis: | 0.90 – 1.10 |
Product Analysis: | 0.85 – 1.15 |
Additional Information:
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Thickness | 5-100mm |
Grade | SA 387 Gr.291 Cl.2 |
Finishing | Hot Rolled Finished |
Condition | New |
Weight | 8.00 |
Density | 8.00 |
Color | Red |
Material | Steel |
Width | 1250-2500 mm |
BS | EN | ASTM/ASME | DIN |
— | — | SA387-91-2 | — |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade 91 | 9.00% | 1.00% |
Designation: | Requirement: |
SA387 Grade 91 | Tensile strength, ksi [MPA] |
Yield strength, min, ksi [MPa]/(0.2% offset) | |
Elongation in 8 in. [200mm], min % | |
Elongation in 2 in. [50mm], min, % | |
Reduction of area, min % |
Additional Information:
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Thickness | 4mm-100mm |
Condition | New |
Density | 8.00 |
Color | Red |
Material | Steel |
Width | 1250-2500 |
Length | 6000-12000mm |
BS | EN | ASTM/ASME | DIN |
621 B | … | SA387-11-2 | … |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade11 | 1.25% | 0.50% |
Element | - | Chemical Composition (%) |
- | SA387 Grade 11 | |
Carbon: | Heat Analysis: | 0.05 – 0.17 |
Product Analysis: | 0.04 – 0.17 | |
Manganese: | Heat Analysis: | 0.40 – 0.65 |
Product Analysis: | 0.35 – 0.73 | |
Phosphorus: | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Sulphur (max): | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Silicon: | Heat Analysis: | 0.50 – 0.80 |
Product Analysis: | 0.44 – 0.86 | |
Chromium: | Heat Analysis: | 1.00 – 1.50 |
Product Analysis: | 0.94 – 1.56 | |
Molybdenum: | Heat Analysis: | 0.45 – 0.65 |
Product Analysis: | 0.45 – 0.70 |
Designation: | Requirement: |
SA387 Grade 11 | Tensile strength, ksi [MPa] |
Yield strength, min, ksi [MPa]/(0.2% offset) | |
Elongation in 8 in. [200mm], min % | |
Elongation in 2 in. [50mm], min, % | |
Reduction of area, min % |
Additional Information:
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Thickness | 5-100mm |
Material Grade | ASME SA SA387 |
Condition | New |
Customization | Customized |
Density | 8.00 |
Material | Steel Plate |
Alloy | With Alloy |
Width | 1250-2500 mm |
BS | EN | ASTM/ASME | DIN |
620 B | 13 CRMO 45 | SA387-12-2 | 13 CRMO 44 |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade12 | 1.00% | 0.50% |
Element | - | Chemical Composition (%) |
- | ASME SA387 Grade 12 | |
Carbon: | Heat Analysis: | 0.05 – 0.17 |
Product Analysis: | 0.04 – 0.17 | |
Manganese: | Heat Analysis: | 0.40 – 0.65 |
Product Analysis: | 0.35 – 0.73 | |
Phosphorus: | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Sulphur (max): | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Silicon: | Heat Analysis: | 0.15 – 0.40 |
Product Analysis: | 0.13 – 0.45 | |
Chromium: | Heat Analysis: | 0.80 – 1.15 |
Product Analysis: | 0.74 – 1.21 | |
Molybdenum: | Heat Analysis: | 0.45 – 0.60 |
Product Analysis: | 0.40 – 0.65 |
Designation: | Requirement: |
SA387 Grade 12 | Tensile strength, ksi [MPA] |
Yield strength, min, ksi [MPa]/(0.2% offset) | |
Elongation in 8 in. [200mm], min % | |
Elongation in 2 in. [50mm], min, % | |
Reduction of area, min % |
Additional Information:
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Thickness | 5-100mm |
Shape | Rectangle |
Finishing | Hot Rolled Finished |
Condition | New |
Customization | Customized |
Weight | 8.00 |
Density | 8.00 |
Color | Reddish |
Material | Steel Plate |
Is It ISO Certified | ISO Certified |
Alloy | With Alloy |
Width | 1250-2500 mm |
BS | EN | ASTM/ASME | DIN |
… | … | SA387-5-2 | … |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade 5 | 5.00% | 0.50% |
Element | - | Chemical Composition (%) |
- | SA 387 Grade 5 | |
Carbon: | Heat Analysis: | 0.15 max |
Product Analysis: | 0.15 max | |
Manganese: | Heat Analysis: | 0.30 – 0.60 |
Product Analysis: | 0.25 – 0.66 | |
Phosphorus: | Heat Analysis: | 0.035 |
Product Analysis: | 0.035 | |
Sulphur (max): | Heat Analysis: | 0.03 |
Product Analysis: | 0.03 | |
Silicon: | Heat Analysis: | 0.50 max |
Product Analysis: | 0.55 max | |
Chromium: | Heat Analysis: | 4.00 – 6.00 |
Product Analysis: | 3.90 – 6.10 | |
Molybdenum: | Heat Analysis: | 0.45 – 0.65 |
Product Analysis: | 0.40 – 0.70 |
Additional Information:
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Grade | SA 387 Gr.9 |
Thickness | 6-150mm |
Finishing | Hot Rolled Finish |
Condition | New |
Customization | Customized |
Weight | 8.00 |
Density | 8.00 |
Brand | Indian |
Material | Steel |
Is It ISO Certified | ISO Certified |
Width | 1250-2500mm |
Length | 6000-12000mm |
BS | EN | ASTM/ASME | DIN |
… | … | SA387-9-2 | … |
Designation | Nominal Chromium Content (%) | Nominal Molybdenum Content (%) |
SA387 Grade 9 | 9.00% | 1.00% |
Element | - | Chemical Composition (%) |
- | SA 387 Grade 9 | |
Carbon: | Heat Analysis: | 0.15 max |
Product Analysis: | 0.15 max | |
Manganese: | Heat Analysis: | 0.30 – 0.60 |
Product Analysis: | 0.25 – 0.66 | |
Phosphorus: | Heat Analysis: | 0.03 |
Product Analysis: | 0.03 | |
Sulphur (max): | Heat Analysis: | 0.03 |
Product Analysis: | 0.03 | |
Silicon: | Heat Analysis: | 1.00 max |
Product Analysis: | 1.05 max | |
Chromium: | Heat Analysis: | 8.00 – 10.00 |
Product Analysis: | 7.90 – 10.10 | |
Molybdenum: | Heat Analysis: | 0.90 – 1.10 |
Product Analysis: | 0.85 – 1.15 | |
Vanadium: | Heat Analysis: | 0.04 max |
Product Analysis: | 0.05 max |
Additional Information:
Grade | C | Si | Mn | P | S | Cr | Mo | Ni | Others |
620B | 0.09/0.18 | 0.15/0.40 | 0.40/0.65 | 0.025 | 0.015 | 0.80/1.15 | 0.45/0.60 | 0.3 | 0.32 |
Grade | Thickness | Tensile Strength | Yield Strength | Elongation (A) |
620B | ≤75 | 480/600 | 340 | 18 |
>75 ≤100 | 450/570 | 280 | 16 | |
>100 ≤150 | 430/550 | 255 | 16 |