Product Details:
Material | Stainless Steel |
Surface Treatment | Cold Rolled |
Standard | ASTM, BS, DIN |
Thickness | 8-12 mm |
Sr. No. | Material | Size | Thickness | Specification |
1 | Mild Steel | 1220 mm x 4880 mm 1500 mm x 6300 mm 2000 mm x 10000mm 2500 mm x 10000mm | 1 mm To 150 mm | IS 2062 |
2 | GI | 1220 mm x 2440 mm 1220 mm x 6000 mm 1500 mm x 6300 mm | 1 mm To 20 mm | DIN, BS, IS & EN Series |
Element | Content |
Carbon, C | 0.25 – 0.290 % |
Copper, Cu | 0.0020 |
Iron, Fe | 98.0 |
Manganese, Mn | 1.03 |
Phosphorous, P | 0.040 % |
Silicon, Si | 0.280 |
Sulfur, S | 0.050 % |
Mechanical Properties | Metric | Imperial |
Tensile Strength, Ultimate | 400 – 550 MPa | 58000 – 79800 psi |
Tensile Strength, Yield | 250 MPa | 36300 psi |
Elongation at Break (in 200 mm) | 0.2 | 0.2 |
Elongation at Break (in 50 mm) | 0.23 | 0.23 |
Modulus of Elasticity | 200 GPa | 29000 ksi |
Bulk Modulus (typical for steel) | 140 GPa | 20300 ksi |
Poissons Ratio | 0.26 | 0.26 |
Shear Modulus | 79.3 GPa | 11500 ksi |
Physical Properties | Metric | Imperial |
Density | 7.85 g/cm3 | 0.284 lb/in3 |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.27 | A, B, C |
over 12.5 to 50 mm | 0.28 | A, B, C | |
over 50 to 100 mm | 0.3 | A, B, C | |
over 100 mm | 0.31 | A, B, C | |
Manganese | 0.85 – 1.20 | A, C | |
0.79 – 1.30 | B, C | ||
Phosphorus (max) | 0.025 | A, B | |
Sulphur (max) | 0.025 | A, B | |
Silicon | 0.15 – 0.40 | A | |
0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 485 – 620 (70 – 90) |
Yield Strength, min MPa (ksi) | 260 (38) |
Elongation min, % 200 mm (8 in) | 17 |
Elongation min, % 50 mm (2 in) | 21 |
Product Details:
Country of Origin | Made in India |