Element | Content (%) |
Iron, Fe | 60 |
Chromium, Cr | 23 |
Nickel, Ni | 14 |
Manganese, Mn | 2 |
Silicon, Si | 1 |
Carbon, C | 0.2 |
Phosphorous, P | 0.045 |
Sulfur, S | 0.03 |
Properties | Metric | Imperial |
Density | 8 g/cm3 | 0.289 lb/in³ |
Melting point | 1455°C | 2650°F |
Properties | Metric | Imperial |
Tensile strength | 620 MPa | 89900 psi |
Yield strength (@ strain 0.200%) | 310 MPa | 45000 psi |
Izod impact | 120 – 165 J | 88.5 – 122 ft-lb |
Shear modulus (typical for steel) | 77 GPa | 11200 ksi |
Elastic modulus | 200 GPa | 29008 ksi |
Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
Elongation at break (in 50 mm) | 0.45 | 0.45 |
Hardness, Brinell | 147 | 147 |
Hardness, Rockwell B | 85 | 85 |
Hardness, Vickers (converted from Rockwell B hardness) | 169 | 169 |
Element | Content (%) |
Iron, Fe | 60 |
Chromium, Cr | 23 |
Nickel, Ni | 14 |
Manganese, Mn | 2 |
Silicon, Si | 1 |
Carbon, C | 0.2 |
Phosphorous, P | 0.045 |
Sulfur, S | 0.03 |
Properties | Metric | Imperial |
Density | 8 g/cm3 | 0.289 lb/in³ |
Melting point | 1455°C | 2650°F |
Properties | Metric | Imperial |
Tensile strength | 620 MPa | 89900 psi |
Yield strength (@ strain 0.200%) | 310 MPa | 45000 psi |
Izod impact | 120 – 165 J | 88.5 – 122 ft-lb |
Shear modulus (typical for steel) | 77 GPa | 11200 ksi |
Elastic modulus | 200 GPa | 29008 ksi |
Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
Elongation at break (in 50 mm) | 0.45 | 0.45 |
Hardness, Brinell | 147 | 147 |
Hardness, Rockwell B | 85 | 85 |
Hardness, Vickers (converted from Rockwell B hardness) | 169 | 169 |