Product Details:
Thickness | 6.3-650mm |
Material Grade | SA516 Gr 60, SA516 Gr 65, SA516 Gr 70, A516 Gr 60, A516 Gr 65, A516 Gr 70 |
Width | 1500-4020mm |
Length | 3000-8000mm |
Base Plate | Cold rolled steel sheet, hot dipped zinc coated steel sheet,hot dipped A-Z coated steel sheet |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.27 | A, B, C |
over 12.5 to 50 mm | 0.28 | A, B, C | |
over 50 to 100 mm | 0.3 | A, B, C | |
over 100 mm | 0.31 | A, B, C | |
Manganese | - | 0.85 – 1.20 | A, C |
- | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 485 – 620 (70 – 90) |
Yield Strength, min MPa (ksi) | 260 (38) |
Elongation min, % 200 mm (8 in) | 17 |
Elongation min, % 50 mm (2 in) | 21 |
Product Details:
Thickness | 4.6-650mm |
Material Grade | SA516 Gr 60, SA516 Gr 65, SA516 Gr 70, A516 Gr 60, A516 Gr 65, A516 Gr 70 |
Width | 1500-4020mm |
Length | 3000-8000mm |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.24 | A, B, C |
over 12.5 to 50 mm | 0.26 | A, B, C | |
over 50 to 100 mm | 0.28 | A, B, C | |
over 100 mm | 0.29 | A, B, C | |
Manganese | - | 0.85 – 1.20 | A, C |
- | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 450 – 585 (65 – 85) |
Yield Strength, min MPa (ksi) | 240 (35) |
Elongation min, % 200 mm (8 in) | 19 |
Elongation min, % 50 mm (2 in) | 23 |
Product Details:
Thickness | 8-650mm |
Width | 1500 - 4020mm |
Length | 3000-8000mm |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.21 | A, B, C |
over 12.5 to 50 mm | 0.23 | A, B, C | |
over 50 to 100 mm | 0.25 | A, B, C | |
over 100 mm | 0.27 | A, B, C | |
Manganese | 12.5 mm and under | 0.60 – 0.90 | A, C, D |
12.5 mm and under | 0.55 – 0.98 | B, C, D | |
over 12.5 mm | 0.85 – 1.20 | A, C | |
over 12.5 mm | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 415 – 550 (60 – 80) |
Yield Strength, min MPa (ksi) | 220 (32) |
Elongation min, % 200 mm (8 in) | 21 |
Elongation min, % 50 mm (2 in) | 25 |
Product Details:
Thickness | 5-650mm |
Width | 1500-4020mm |
Length | 3000-8000mm |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.24 | A, B, C |
over 12.5 to 50 mm | 0.26 | A, B, C | |
over 50 to 100 mm | 0.28 | A, B, C | |
over 100 mm | 0.29 | A, B, C | |
Manganese | - | 0.85 – 1.20 | A, C |
- | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 450 – 585 (65 – 85) |
Yield Strength, min MPa (ksi) | 240 (35) |
Elongation min, % 200 mm (8 in) | 19 |
Elongation min, % 50 mm (2 in) | 23 |
Product Details:
Thickness | 7.2-650mm |
Width | 1500-4020mm |
Length | 3000-8000mm |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.21 | A, B, C |
over 12.5 to 50 mm | 0.23 | A, B, C | |
over 50 to 100 mm | 0.25 | A, B, C | |
over 100 mm | 0.27 | A, B, C | |
Manganese | 12.5 mm and under | 0.60 – 0.90 | A, C, D |
12.5 mm and under | 0.55 – 0.98 | B, C, D | |
over 12.5 mm | 0.85 – 1.20 | A, C | |
over 12.5 mm | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 415 – 550 (60 – 80) |
Yield Strength, min MPa (ksi) | 220 (32) |
Elongation min, % 200 mm (8 in) | 21 |
Elongation min, % 50 mm (2 in) | 25 |
Product Details:
Thickness | 5.1-650mm |
Width | 1500-4020mm |
Length | 3000-8000mm |
Element | Thickness | Composition (%) | Note |
Carbon (max) | 12.5 mm and under | 0.27 | A, B, C |
over 12.5 to 50 mm | 0.28 | A, B, C | |
over 50 to 100 mm | 0.3 | A, B, C | |
over 100 mm | 0.31 | A, B, C | |
Manganese | - | 0.85 – 1.20 | A, C |
- | 0.79 – 1.30 | B, C | |
Phosphorus (max) | - | 0.025 | A, B |
Sulphur (max) | - | 0.025 | A, B |
Silicon | - | 0.15 – 0.40 | A |
- | 0.13 – 0.45 | B |
Mechanical Property | Value |
Tensile Strength, MPa (ksi) | 485 – 620 (70 – 90) |
Yield Strength, min MPa (ksi) | 260 (38) |
Elongation min, % 200 mm (8 in) | 17 |
Elongation min, % 50 mm (2 in) | 21 |
Product Details:
Minimum Order Quantity | 20 Kilogram |
Material | Steel |
Thickness | 15,16,43,63,29 mm |
HRB | BS 1501.224.490 |